Reasonable price Fkm Seal Material - General Purpose Fluoroelastomer Base Polymer – FUDI

short description:

Stock Sample is Free & Available

Send email to us Whatsapp Email

Product Detail

Product Tags

Feedback (2)

All we do is usually connected with our tenet " Customer to start with, Rely on initial, devoting on the food packaging and environmental protection for Rubber Fpm, Fluoropolymer Tube, Ptfe Dry Lubricant Powder, And we are able to enable on the lookout for any products with the customers' needs. Make sure deliver the best Assistance, the most beneficial High-quality, The quickly Delivery.

Reasonable price Fkm Seal Material - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:

Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.

FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.

Items	Grades
	FD2601	FD2602	FD2603	FD2604	FD2605
Density (g/cm³)	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02
Fluorine content (%)	66	66	66	66	66
Mooney Viscosity (ML (1+10)121℃)	25	40~45	60~70	>100	150
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥13	≥13
Elongation at break after post cure (%)24h, 230℃	≥180	≥150	≥150	≥150	≥150
Compression set (%) 70h, 200℃	≤25

FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.

	FD2462	FD2463	FD2465	FD2465L	FD2465H
Fluorine Content	68.5	68.5	68.5	65	69.5
Density (g/cm³)	1.85	1.85	1.85	1.81	1.88
Mooney Viscosity (ML (1+10)121℃)	70±10	40±10	45±15	50±10	40±20
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥11	≥11
Elongation at break after post cure (%)24h, 230℃	≥180	≥180	≥180	≥180	≥180
Compression set (%) 200℃ 70H compress 20%	≤30%	≤30%	≤30%	≤30%	≤40%
Oil resistance (200℃ 24H) RP-3 oil	≤5%	≤5%	≤5%	≤5%	≤2%
Glass transition temperature (TG)	＞-15℃	＞-15℃	＞-15℃	＞-21℃	＞-13℃
Water content (%)	≤0.15	≤0.15	≤0.15	≤0.15	≤0.15

Package and Storage

Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs

Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.

Product detail pictures:

Related Product Guide:

To meet the customers' over-expected satisfaction , we have our strong team to provide our best overall service which includes marketing, sales, designing, production, quality controlling, packing, warehousing and logistics for Reasonable price Fkm Seal Material - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Johannesburg, Lithuania, Libya, With the enterprising spirit of" high efficiency, convenience, practicality and innovation", and in line with such serving guidance of "good quality but better price, " and "global credit", we've been striving to cooperate with the automobile parts companies all over the world to make a win-win partnership.

Dowhon Fkm