Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.
FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.
|
Items |
Grades |
||||
| FD2601 | FD2602 | FD2603 | FD2604 | FD2605 | |
| Density (g/cm3) | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 |
| Fluorine content (%) | 66 | 66 | 66 | 66 | 66 |
| Mooney Viscosity (ML (1+10)121℃) | 25 | 40~45 | 60~70 | >100 | 150 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥13 | ≥13 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥150 | ≥150 | ≥150 | ≥150 |
| Compression set (%) 70h, 200℃ |
≤25 |
||||
FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.
| FD2462 | FD2463 | FD2465 | FD2465L | FD2465H | |
| Fluorine Content | 68.5 | 68.5 | 68.5 | 65 | 69.5 |
| Density (g/cm3) | 1.85 | 1.85 | 1.85 | 1.81 | 1.88 |
| Mooney Viscosity (ML (1+10)121℃) | 70±10 | 40±10 | 45±15 | 50±10 | 40±20 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥11 | ≥11 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥180 | ≥180 | ≥180 | ≥180 |
| Compression set (%) 200℃ 70H compress 20% | ≤30% | ≤30% | ≤30% | ≤30% | ≤40% |
| Oil resistance (200℃ 24H) RP-3 oil | ≤5% | ≤5% | ≤5% | ≤5% | ≤2% |
| Glass transition temperature (TG) | ＞-15℃ | ＞-15℃ | ＞-15℃ | ＞-21℃ | ＞-13℃ |
| Water content (%) | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 |
Package and Storage
Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs
Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.
Product detail pictures:
Related Product Guide:
"Sincerity, Innovation, Rigorousness, and Efficiency" is the persistent conception of our firm to the long-term to develop together with consumers for mutual reciprocity and mutual advantage for New Arrival China Fkm Rubber Material Properties - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Surabaya, Monaco, Hungary, Our solutions have national accreditation standards for experienced, premium quality goods, affordable value, was welcomed by people around the globe. Our products will continue to increase in the order and look forward to cooperation with you, Truly must any of people goods be of interest to you, make sure you letus know. We're likely to be delighted to give you a quotation up on receipt of one's in depth specs.
By Audrey from Chile - 2018.02.08 16:45
This is a honest and trustworthy company, technology and equipment are very advanced and the prodduct is very adequate, there is no worry in the suppliment.
By Rae from Albania - 2017.09.22 11:32