Our eternal pursuits are the attitude of "regard the market, regard the custom, regard the science" as well as theory of "quality the basic, have faith in the initial and administration the advanced" for Catalyst 5, Viton Rubber Properties, Ffkm, We are keeping durable small business relationships with additional than 200 wholesalers in the USA, the UK, Germany and Canada. For anyone who is intrigued in any of our products, make sure you experience free to speak to us.

Hot New Products Fkm Sheet - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:

Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.

FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.

Items	Grades
	FD2601	FD2602	FD2603	FD2604	FD2605
Density (g/cm³)	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02
Fluorine content (%)	66	66	66	66	66
Mooney Viscosity (ML (1+10)121℃)	25	40~45	60~70	>100	150
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥13	≥13
Elongation at break after post cure (%)24h, 230℃	≥180	≥150	≥150	≥150	≥150
Compression set (%) 70h, 200℃	≤25

FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.

	FD2462	FD2463	FD2465	FD2465L	FD2465H
Fluorine Content	68.5	68.5	68.5	65	69.5
Density (g/cm³)	1.85	1.85	1.85	1.81	1.88
Mooney Viscosity (ML (1+10)121℃)	70±10	40±10	45±15	50±10	40±20
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥11	≥11
Elongation at break after post cure (%)24h, 230℃	≥180	≥180	≥180	≥180	≥180
Compression set (%) 200℃ 70H compress 20%	≤30%	≤30%	≤30%	≤30%	≤40%
Oil resistance (200℃ 24H) RP-3 oil	≤5%	≤5%	≤5%	≤5%	≤2%
Glass transition temperature (TG)	＞-15℃	＞-15℃	＞-15℃	＞-21℃	＞-13℃
Water content (%)	≤0.15	≤0.15	≤0.15	≤0.15	≤0.15

Package and Storage

Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs

Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.

Product detail pictures:

Related Product Guide:

Having a sound small business credit score, outstanding after-sales services and modern manufacturing facilities, we've got earned an fantastic reputation among our buyers across the globe for Hot New Products Fkm Sheet - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Netherlands, Netherlands, America, With the spirit of "credit first, development through innovation, sincere cooperation and joint growth", our company is striving to create a brilliant future with you, so as to become a most valuable platform for exporting our goods in China!