High reputation Viton Fkm Material - General Purpose Fluoroelastomer Base Polymer – FUDI

short description:


Stock Sample is Free & Available

Product Detail

Product Tags

Related Video

Feedback (2)

In the past few years, our company absorbed and digested advanced technologies both at home and abroad. Meanwhile, our company staffs a team of experts devoted to the development of Kalrez Ffkm, fluorosilicone polymer, Viton Gasket Sheet, Any needs from you'll be paid out with our best notice!
High reputation Viton Fkm Material - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:

Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.

FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.

Items

Grades

FD2601 FD2602 FD2603 FD2604 FD2605
Density (g/cm3) 1.82±0.02 1.82±0.02 1.82±0.02 1.82±0.02 1.82±0.02
Fluorine content (%) 66 66 66 66 66
Mooney Viscosity (ML (1+10)121℃) 25 40~45 60~70 >100 150
Tensile strength after post cure (Mpa) 24h, 230℃ ≥11 ≥11 ≥11 ≥13 ≥13
Elongation at break after post cure (%)24h, 230℃ ≥180 ≥150 ≥150 ≥150 ≥150
Compression set (%) 70h, 200℃

≤25

FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.

FD2462 FD2463 FD2465 FD2465L FD2465H
Fluorine Content 68.5 68.5 68.5 65 69.5
Density (g/cm3) 1.85 1.85 1.85 1.81 1.88
Mooney Viscosity (ML (1+10)121℃) 70±10 40±10 45±15 50±10 40±20
Tensile strength after post cure (Mpa) 24h, 230℃ ≥11 ≥11 ≥11 ≥11 ≥11
Elongation at break after post cure (%)24h, 230℃ ≥180 ≥180 ≥180 ≥180 ≥180
Compression set (%) 200℃ 70H compress 20% ≤30% ≤30% ≤30% ≤30% ≤40%
Oil resistance (200℃ 24H) RP-3 oil ≤5% ≤5% ≤5% ≤5% ≤2%
Glass transition temperature (TG) >-15℃ >-15℃ >-15℃ >-21℃ >-13℃
Water content (%) ≤0.15 ≤0.15 ≤0.15 ≤0.15 ≤0.15

Package and Storage

Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs

Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.


Product detail pictures:

High reputation Viton Fkm Material - General Purpose Fluoroelastomer Base Polymer – FUDI detail pictures

High reputation Viton Fkm Material - General Purpose Fluoroelastomer Base Polymer – FUDI detail pictures

High reputation Viton Fkm Material - General Purpose Fluoroelastomer Base Polymer – FUDI detail pictures


Related Product Guide:

Our commission should be to provide our customers and consumers with ideal top quality and aggressive portable digital products for High reputation Viton Fkm Material - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Borussia Dortmund, Guatemala, Bolivia, We also provide OEM service that caters to your specific needs and requirements. With a strong team of experienced engineers in hose design and development, we value every opportunity to provide best products and solutions for our customers.
  • The manufacturer gave us a big discount under the premise of ensuring the quality of products, thank you very much, we will select this company again.
    5 Stars By Beatrice from Romania - 2018.11.02 11:11
    Superb technology, perfect after-sales service and efficient work efficiency, we think this is our best choice.
    5 Stars By Karen from United States - 2017.04.08 14:55
    Write your message here and send it to us