High Quality Fkm Rubber Material - General Purpose Fluoroelastomer Base Polymer – FUDI
Stock Sample is Free & Available
High Quality Fkm Rubber Material - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:
Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.
FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.
|
Items |
Grades |
||||
| FD2601 | FD2602 | FD2603 | FD2604 | FD2605 | |
| Density (g/cm3) | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 |
| Fluorine content (%) | 66 | 66 | 66 | 66 | 66 |
| Mooney Viscosity (ML (1+10)121℃) | 25 | 40~45 | 60~70 | >100 | 150 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥13 | ≥13 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥150 | ≥150 | ≥150 | ≥150 |
| Compression set (%) 70h, 200℃ |
≤25 |
||||
FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.
| FD2462 | FD2463 | FD2465 | FD2465L | FD2465H | |
| Fluorine Content | 68.5 | 68.5 | 68.5 | 65 | 69.5 |
| Density (g/cm3) | 1.85 | 1.85 | 1.85 | 1.81 | 1.88 |
| Mooney Viscosity (ML (1+10)121℃) | 70±10 | 40±10 | 45±15 | 50±10 | 40±20 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥11 | ≥11 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥180 | ≥180 | ≥180 | ≥180 |
| Compression set (%) 200℃ 70H compress 20% | ≤30% | ≤30% | ≤30% | ≤30% | ≤40% |
| Oil resistance (200℃ 24H) RP-3 oil | ≤5% | ≤5% | ≤5% | ≤5% | ≤2% |
| Glass transition temperature (TG) | ＞-15℃ | ＞-15℃ | ＞-15℃ | ＞-21℃ | ＞-13℃ |
| Water content (%) | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 |
Package and Storage
Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs
Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.
Product detail pictures:
Related Product Guide:
Using a total scientific good quality management process, superior high quality and excellent faith, we get great name and occupied this field for High Quality Fkm Rubber Material - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Germany, Paris, Danish, They're durable modeling and promoting effectively all over the world. Under no circumstances disappearing major functions in a quick time, it's a should for you of excellent good quality. Guided by the principle of "Prudence, Efficiency, Union and Innovation. the company make a terrific efforts to expand its international trade, raise its company profit and raise its export scale. We're confident that we are going to possess a vibrant prospect and to be distributed all over the world within the years to come.
By Clementine from Latvia - 2018.06.03 10:17
This company has the idea of "better quality, lower processing costs, prices are more reasonable", so they have competitive product quality and price, that's the main reason we chose to cooperate.
By Lillian from Libya - 2017.01.28 19:59