Good Wholesale Vendors Ffkm Elastomer - General Purpose Fluoroelastomer Base Polymer – FUDI

short description:

Stock Sample is Free & Available

Send email to us Whatsapp Email

Product Detail

Product Tags

Feedback (2)

With advanced technologies and facilities, strict high-quality handle, reasonable rate, superior services and close co-operation with prospects, we are devoted to furnishing the best price for our customers for Viton Flange Gasket, Viton Extrusion, Viton Tube, Create Values,Serving Customer!" is the aim we pursue. We sincerely hope that all customers will establish long term and mutually beneficial cooperation with us.If you wish to get more details about our company, Please contact with us now.

Good Wholesale Vendors Ffkm Elastomer - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:

Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.

FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.

Items	Grades
	FD2601	FD2602	FD2603	FD2604	FD2605
Density (g/cm³)	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02
Fluorine content (%)	66	66	66	66	66
Mooney Viscosity (ML (1+10)121℃)	25	40~45	60~70	>100	150
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥13	≥13
Elongation at break after post cure (%)24h, 230℃	≥180	≥150	≥150	≥150	≥150
Compression set (%) 70h, 200℃	≤25

FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.

	FD2462	FD2463	FD2465	FD2465L	FD2465H
Fluorine Content	68.5	68.5	68.5	65	69.5
Density (g/cm³)	1.85	1.85	1.85	1.81	1.88
Mooney Viscosity (ML (1+10)121℃)	70±10	40±10	45±15	50±10	40±20
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥11	≥11
Elongation at break after post cure (%)24h, 230℃	≥180	≥180	≥180	≥180	≥180
Compression set (%) 200℃ 70H compress 20%	≤30%	≤30%	≤30%	≤30%	≤40%
Oil resistance (200℃ 24H) RP-3 oil	≤5%	≤5%	≤5%	≤5%	≤2%
Glass transition temperature (TG)	＞-15℃	＞-15℃	＞-15℃	＞-21℃	＞-13℃
Water content (%)	≤0.15	≤0.15	≤0.15	≤0.15	≤0.15

Package and Storage

Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs

Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.

Product detail pictures:

Related Product Guide:

We support our buyers with ideal high quality products and high level service. Becoming the specialist manufacturer in this sector, we have gained rich practical experience in producing and managing for Good Wholesale Vendors Ffkm Elastomer - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Chile, America, UK, Ought to any of these products be of curiosity to you, remember to allow us to know. We are going to be satisfied to give you a quotation on receipt of one's in depth specs. We've our private experienced R&D enginners to meet any of one's requriements, We appear forward to receiving your enquires soon'and hope to have the opportunity to work together with you in the future. Welcome to check out our company.

Ffkm Gasket